分别以Bi(NO3)3和Na2WO4溶液直接混合所得沉淀、加氨水所得沉淀及Bi(NO3)3×5H2O+Na2WO4×2H2O为前驱体，采用熔盐法合成Bi2WO6光催化剂粉体，研究了不同前驱体所制粉体的物相、形貌，以其为催化剂，在可见光照射下降解罗丹明B溶液. 结果表明，用后二者为前驱体均可得到薄片状纯相Bi2WO6粉体. 加氨水所得沉淀为前驱体所制Bi2WO6粉体的光催化性能最好，在可见光照射下对0.01 mmol/L RhB溶液的降解率在60 min内达99%.

Bi2WO6 photocatalyst powder was synthesized by molten salt method using precipitate from mixed Bi(NO3)3 and Na2WO4 aqueous solutions with and without addition of ammonia, commercial Bi(NO3)3×5H2O and Na2WO4×2H2O as precursors, respectively. The effects of precursors on the phase composition, morphology and degradation of RhB under visible light were examined. The results indicated that pure flake-like Bi2WO6 powder could be prepared from two precursors: precipitate from mixed Bi(NO3)3 and Na2WO4 aqueous solutions with addition of ammonia solution, and commercial Bi(NO3)3×5H2O+Na2WO4×2H2O. Bi2WO6 powder originated from the former precursor performed better on the photocatalytic degradation of RhB, which could degrade 0.01 mmol/L RhB almost completely (99%) under visible light irradiation within 60 min.