用高氯酸盐前躯体制备普鲁士蓝(PB)材料，考察了合成过程中前驱体成分、溶液温度、钠盐添加量及杂质含量对材料性能的影响. 结果表明，氯化亚铁作铁源时，不清洗的普鲁士蓝产物中含NaCl杂质，电化学性能明显低于经多次清洗的产物；高氯酸亚铁作铁源时，不清洗直接收集的普鲁士蓝产物初始放电容量略低于清洗产物，但长期循环稳定性更好，免清洗工艺可明显提高普鲁士蓝材料的收率，少量高氯酸钠杂质存在提高了材料的循环性能.
A high yield preparation method for prussian blue (PB) by using perchlorate precursors was explored. The influence of compositions of the precursor solution, preparation temperature, sodium salt addition and impurities in the final products on the electrochemical properties of final PB products were investigated. The results showed that the existence of impurities lead to a slight decrease of specific capacity. For PB material prepared using FeCl2 precursor, electrochemical performance of the unwashed sample was obvious inferior to that of the washed sample due to the existence of NaCl impurity. On the other hand, for the PB material prepared by using Fe(ClO4)2 precursor, initial discharge capacity of PB product without being clean washed was slightly lower than being washed but showed better cycling stability due to the existence of small amount of NaClO4 impurity. The unwash synthesis route leads to a high yield of PB product.
[1]Il Park S, Gocheva I.Okada S,et al..Electrochemical Properties of NaTi2(PO4)(3) Anode for Rechargeable Aqueous Sodium-ion Batteries[J].Journal of the Electrochemical Society, 2011, 158(10):A1067-A1070
[2]Kawabe Y, Yabuuchi N.Kajiyama M,et al..Synthesis and Electrode Performance of Carbon Coated Na2FePO4F for Rechargeable Na Batteries[J].Electrochemistry Communications, 2011, 13(11):1225-1228
[3]Komaba S, Murata W.Ishikawa T,et al..Electrochemical Na Insertion and Solid Electrolyte Interphase for Hard-carbon Electrodes and Application to Na-ion Batteries[J].Advanced Functional Materials, 2011, 21(20):3859-3867
[4]Komaba S, Takei C.Nakayama T,et al..Electrochemical Intercalation Activity of Layered NaCrO2 vs. LiCrO2[J].Electrochemistry Communications, 2010, 12(3):355-358
[5]Lu Y.H.,Wang L,Cheng J. G.,et al..Prussian blue: a New Framework of Electrode Materials for Sodium Batteries[J].Chemical Communications, 2012, 48(52):6544-6546
[6]Qian J.F.,Zhou M,Cao Y. L.,et al..Nanosized Na4Fe(CN)6C Composite as a Low-cost and High-rate Cathode Material for Sodium-ion Batteries[J].Advanced Energy Materials, 2012, 2(4):410-414
[7]Komabaa S, Nakayamaa T.Ogataa A.Electrochemically Reversible Sodium Intercalation of Layered NaNi0.5Mn0.5O2 and NaCrO2[J].The Electrochemical Society, 2009, 16(42):43-45
[8]Mu L.Q.,Xu SY.,Li Y. M.,et al..Prototype Sodium-ion Batteries Using an Air-stable and CoNi-free O-3-layered Metal Oxide Cathode[J].Advanced Materials, 2015, 27(43):6928-+
[9]Zhang Q.Wang W,Wang Y. J.,et al..Controllable Construction of 3D-skeleton-carbon Coated Na3V2(PO4)(3) for High-Performance Sodium ion Battery Cathode[J].Nano Energy, 2016, 20:11-19
[10]Yang Y.Liu ES.,Yan X. M.,et al..Influence of Structural Imperfection on Electrochemical Behavior of Prussian Blue Cathode Materials for Sodium ion Batteries[J].Journal Of the Electrochemical Society,2016, 163(9):A2117-A2123
[11]Chen J.Ding ZY.,Wang C.,et al..Black Anatase Titania with Ultrafast Sodium-storage Performances Stimulated by Oxygen Vacancies[J].Acs Applied Materials & Interfaces, 2016, 8(14):9142-9151
[12] Wessells C.D., Huggins R. A., Cui Y., et al..Copper Hexacyanoferrate Battery Electrodes with Long Cycle Life and High Power [J].Nature Communications, 2011（2）.
[13]杨汉西，钱江锋.水溶液钠离子电池及其关键材料的研究进展[J].无机材料学报, 2013, 28(11):1165-
[14]You Y, Wu X.L.,Yin YX.,et al..High-quality Prussian Blue Crystals as Superior Cathode Materials for Room-temperature Sodium-ion Batteries[J].Energy & Environmental Science, 2014, 7(5):1643-1647
[15]Yang D.Z.,Liao XZ,Huang B. W.,et al. A Na4Fe(CN)6NaCl Solid Solution Cathode Material with an Enhanced Electrochemical Performance for Sodium ion Batteries[J].Journal of Material Chemistry A, 2013, 1(42):13417-13421
[16]Yang D.Z.,Xu J,Liao XZ.,et al. Structure Optimization of Prussian Blue Analogue Cathode Materials for Advanced Sodium ion Batteries[J].Chemical Communication., 2014, 50(87):13377-13380
[17]Yan X.M.,Yang Y,Liu E. S.,et al..Improved Cycling Performance of Prussian Blue Cathode for Sodium ion Batteries by Controlling Operation Voltage Range[J].Electrochemica Acta, 2017, 225:235-242