纳米零价铁对水溶液中钒离子的吸附性能

赵长多 范美玲 杨晓博 胡文斌 夏启斌

doi:10.12034/j.issn.1009-606X.217434

过程工程学报 >

2018 , Vol. 18 >Issue 6: 1253 - 1260

DOI: https://doi.org/10.12034/j.issn.1009-606X.217434

过程与工艺

纳米零价铁对水溶液中钒离子的吸附性能

赵长多范美玲杨晓博胡文斌夏启斌

展开

1. 华南理工大学化学与化工学院，广东广州 510640 2. 广东省粤电集团有限公司安全监察及生产技术部，广东广州 510630

收稿日期: 2017-12-15

修回日期: 2018-04-08

网络出版日期: 2018-12-19

基金资助

广东省科技计划项目（公益研究与能力建设）

收起

Adsorption of vanadium ion in solution on nano zero-valent irons

Changduo ZHAO Xiaobo YANG Meiling FAN Wenbin HU Qibin XIA

Expand

1. South China University of Technology, Guangzhou, Guangdong 510640, China 2. Safety Supervision and Production Technology of Guangdong Yudean Group Co., Ltd., Guangzhou, Guangdong 510630, China

Received date: 2017-12-15

Revised date: 2018-04-08

Online published: 2018-12-19

Fold

摘要

采用液相还原法制备纳米零价铁(nZVI)，采用PXRD, SEM, TEM, BET(N2吸脱附)和XPS等表征材料性能，考察了纳米零价铁用量、初始钒(V)浓度和初始pH对纳米零价铁吸附钒(V)性能的影响，测定了纳米零价铁对钒(V)的吸附等温线和吸附动力学曲线. 结果表明，制备的纳米零价铁具有典型的核?壳结构，粒径为10~30 nm，BET比表面积为53 m2/g. 纳米零价铁对钒(V)的吸附容量随纳米零价铁用量和初始pH增大而减小. 25℃时的平衡吸附容量为227.8 mg/g. Langmuir等温线方程可很好拟合纳米零价铁对钒(V)的吸附，纳米零价铁对钒(V)的吸附动力学曲线符合准二级动力学模型.

关键词： 关键词:SCR催化剂; 纳米零价铁; 钒; 吸附; 热力学; 动力学

本文引用格式

赵长多范美玲杨晓博胡文斌夏启斌 . 纳米零价铁对水溶液中钒离子的吸附性能[J]. 过程工程学报, 2018 , 18(6) : 1253 -1260 . DOI: 10.12034/j.issn.1009-606X.217434

Abstract

Nano zero-valent iron (nZVI) was synthesized by the liquid-phase reduction method, and characterized by powder X-ray diffraction (PXRD), scanning electron microscope (SEM), transmission electron microscope (TEM), the Brunauer-Emmett-Teller (BET) and X-ray photoelectron spectroscopy (XPS) method. The adsorption performance of vanadium (V) on nZVI was investigated by rationally adjusting the parameters, such as additive amount of nZVI, initial concentration of vanadium(V) and initial pH value. Additionally, the adsorption isotherms and kinetic curves of vanadium(V) on nZVI were measured. The results showed that nZVI exhibited a regular core?shell structure with an average particle size of 10~30 nm and the BET surface area of 53 m2/g. Furthermore, the adsorption capacity of vanadium(V) decreased with the increase in initial pH value and nZVI amount added, respectively. The maximum vanadium(V) adsorption capacity reached 227.8 mg/g at 25℃. The adsorption isotherms of vanadium(V) on nZVI fitted well with Langmuir model, and the adsorption kinetics of vanadium(V) on nZVI could be well described by a pseudo-second-order kinetic model. The nZVI synthesized in this work will provide an useful insights into the comprehensive utilization of waste SCR denitration catalyst.

Key words： Keywords : SCR catalyst; nZVI; vanadium; adsorption; thermodynamics; kinetics

参考文献

[1] Khodayari R, Odenbrand C U I. Regeneration of commercial TiO2-V2O5-WO3 SCR catalysts used in bio fuel plants [J]. Environmental, 2001, 30: 87-99.
[2] 段竞芳, 史伟伟, 夏启斌, 等. 失活钒钛基SCR催化剂性能表征及其再生[J]. 功能材料. 2012(16):2191-5.Duan J F ,Shi W W, Xia Q B , et, al. Characterization and regeneration of deactivated commercial SCR catalyst. [J]. Journal of Functional Materials. 2012(16):2191-5.
[3] Amiridis M.D, Duevel R.V., Wachs I.E. The effect of metal oxide additives on the activity of V2O5/TiO2 catalysts for the selective catalytic reduction of nitric oxide by ammonia[J]. Appl Catal B-Environ, 1999, 20(2): 11-22.
[4] Finocchio E, Baldi M, Busca G, Pistarino C, Romezzano G, Bregani F, et al. A study of the abatement of VOC over V2O5-WO3-TiO2 and alternative SCR catalyst [J]. Catalysis Today, 2000, 59(3): 261-268.
[5] 曾瑞. 有关我国SCR废催化剂回收产业的思考[J] .中国环保产业.2013(04): 55-61.Zeng R. Consideration on Reclaiming Industry of SCR Waste Catalyzer in China[J]. China Environmental Protection Industry.2013(04): 55-61.
[6] Choung J.W., Nam I.S., Ham S.W. Effect of promoters including tungsten and barium on the thermal stability of V2O5/sulfated TiO2 catalyst for NO reduction by NH3[J]. Catalysis Today, 2006,111(3-4): 242-247.
[7] 中国环境保护产业协会脱硫脱硝委员会,北京. 脱硫脱硝行业2015年发展综述[J]. 中国环保产业, 2017(1):6-21.Desulfurization and Denitration Committee of CAEPI, Beijing. Development Report on Desulfurization and Denitration Industries in 2015[J]. China Environmental Protection Industry,2017(1):6-21.
[8] Zeng L, Cheng C.Y.. A literature review of the recovery of molybdenum and vanadium from spent hydrodesulphurisation catalysts[J]. Hydrometallurgy, 2009, 98(1-2): 1-20.
[9] 张琛, 刘建华, 杨晓博. 超声强化废SCR催化剂浸出V和W的研究[J]. 功能材料, 2015, 20(46): 20063-20067.Zhang C, Liu J H Yang X B .Ultrasound assited enhancement in vanadium and tungsten leaching from waste SCR catalyst[J]. Journal of Functional Materials,2015, 20(46): 20063-20067.
[10] 朱跃, 何胜, 张扬. 从废烟气脱硝催化剂中回收金属氧化物的方法, CN 101921916 A[P]. 2010.Zhu Y, He S, Zhang Y. Method for recovering metal oxide from waste flue gas denitrification catalyst, CN 101921916 A[P]. 2010.
[11] 霍怡廷, 常志东, 董彬, 等. 一种SCR废烟气脱硝催化剂的回收方法,CN 103526031 A [P].2014.Huo Y T, Chang Z D, Dong B, et, al. Method for recovering spend SCR catalyst, CN 103526031 A [P].2014.
[12] 刘清雅，刘振宇，李启超. 一种从废弃钒钨钛基催化剂中回收钒、钨和钛的方法, CN 103484678 A [P].2014.Liu Q Y, Liu Z Y, Li Q C. Method for recovering V, W andTi from spent V W-Ti-based catalyst, CN 103484678 A [P].2014
[13] 宋阜, 朱宾权. 离子交换法分离富集钨酸钠溶液中的钒[J]. 稀有金属与硬质合金, 2006, 34(03): 5-11.Song F, Zhu B Q. Extraction of Vanadium from Sodium Tungstats by Ion Exchange[J]. Rare Metals and Cemented Carbides, 2006, 34(03): 5-11.
[14] Nguyen T H, Man S L. Recovery of molybdenum and vanadium with high purity from sulfuric acid leach solution of spent hydrodesulfurization catalysts by ion exchange[J]. Hydrometallurgy, 2014, 147-148(8):142-147.
[15] Nguyen T H, Man S L. Separation of Vanadium and Tungsten from Sodium Molybdate Solution by Solvent Extraction[J]. Ind.eng.chem.res, 2014, 53(20):8608-8614.
[16] Neková? P, Schr?tterová D. Extraction of V(V), Mo(VI) and W(VI) polynuclear species by primene JMT[J]. Chemical Engineering Journal, 2000, 79(3):229-233.
[17] 刘梦, 王华静, 王鲲鹏, 等. 腐植酸对水体中五价钒的吸附[J]. 农业环境科学学报, 2016, 35 (5): 969-975.Liu M, Wang H J, Wang K P, et al. Adsorption of pentavalent vanadium by humic acid in water[J]. Journal of Agro-Environment Science,2016, 35（5）: 969-975.
[18] Luo L, Miyazaki T, Shibayama A, et al. A novel process for recovery of tungsten and vanadium from a leach solution of tungsten alloy scrap[J]. Minerals Engineering, 2003, 16(7):665-670.
[19] 阳亚玲, 颜文斌, 高峰. 离子交换树脂分离钒渣浸出液中钒与铬[J]. 过程工程学报, 2017, 17(01):84-91.Yang Y L, Yan W B, Gao F. Separation of V2O5 and Cr(VI) from Vanadium Slag Leaching Solution by Ion Exchange Resin[J]. The Chinese Journal of Process Engineering, 2017, 17(01):84-91.
[20] Zhang L, Liu X, Xia W, et al. Preparation and characterization of chitosan-zirconium(IV) composite for adsorption of vanadium(V).[J]. International Journal of Biological Macromolecules, 2014, 64(2):155-161.
[21] Crane R A, Scott T B. Nanoscale zero-valent iron: future prospects for an emerging water treatment technology[J]. Journal of Hazardous Materials, 2012, s 211–212(211-212):112-125.
[22] Liu, T., Z. Wang and Y. Sun, Manipulating the morphology of nanoscale zero-valent iron on pumice for removal of heavy metals from wastewater. Chemical Engineering Journal, 2015. 263: p. 55-61.
[23] Habish, A.J., et al., Nanoscale zerovalent iron (nZVI) supported by natural and acid-activated sepiolites: the effect of the nZVI/support ratio on the composite properties and Cd2+ adsorption. Environmental Science and Pollution Research, 2017. 24(1): p. 628-643.
[24] Qian, L., et al., Nanoscale zero-valent iron supported by biochars produced at different temperatures: Synthesis mechanism and effect on Cr(VI) removal. Environmental Pollution, 2017. 223: p. 153-160.
[25] Petala, E., et al., Nanoscale zero-valent iron supported on mesoporous silica: Characterization and reactivity for Cr(VI) removal from aqueous solution. Journal of Hazardous Materials, 2013. 261: p. 295-306.
[26] Shi, L., X. Zhang and Z. Chen, Removal of Chromium (VI) from wastewater using bentonite-supported nanoscale zero-valent iron. Water Research, 2011. 45(2): p. 886-892.
[27] Liu, T., et al., Removal of mercury (II) and chromium (VI) from wastewater using a new and effective composite: Pumice-supported nanoscale zero-valent iron. Chemical Engineering Journal, 2014. 245: p. 34-40.
[28] Chen, W., et al., Recovery of indium ions by nanoscale zero-valent iron. Journal of Nanoparticle Research, 2017. 19(3).
[29] Petala E, Dimos K, Douvalis A, et al. Nanoscale zero-valent iron supported on mesoporous silica: characterization and reactivity for Cr(VI) removal from aqueous solution[J]. Journal of Hazardous Materials, 2013, 261(13):295-306.
[30] Liu A, Liu J, Han J, et al. Evolution of nanoscale zero-valent iron (nZVI) in water: Microscopic and spectroscopic evidence on the formation of nano- and micro-structured iron oxides[J]. Journal of Hazardous Materials, 2017, 322(Pt A):129.
[31] Azizian S. Kinetic models of sorption: a theoretical analysis[J]. Journal of Colloid & Interface Science, 2004, 276(1):47.
[32] Boparai H K, Joseph M, O'Carroll D M. Kinetics and thermodynamics of cadmium ion removal by adsorption onto nano zerovalent iron particles.[J]. Journal of Hazardou s Materials, 2011, 186(1):458-65.
[33] Sun Y.P., Li X.Q., Cao J.S., et al. Characterization of zero-valent iron nanoparticles[J]. Advances in Colloid and Interface Science, 2006, 120(1): 47-56.
[34] Li S, Wang W, Liang F, et al. Heavy metal removal using nanoscale zero-valent iron (nZVI): Theory and application.[J]. Journal of Hazardous Materials, 2016, 322:163-171.
[35] Peacock C L, Sherman D M. Vanadium(V) adsorption onto goethite (α-FeOOH) at pH 1.5 to 12: a surface complexation model based on ab initio molecular geometries and EXAFS spectroscopy[J]. Geochimica Et Cosmochimica Acta, 2004, 68(8):1723-1733.

Options

文章导航

模态框（Modal）标题

摘要

本文引用格式

Abstract

参考文献