通过研究不锈钢酸洗废水体系中氟离子脱除和金属离子沉淀的规律，开发了钙钠协同沉淀新工艺，并对新工艺产生的污泥于1200℃下进行还原，细磨、磁选后得铁、铬、镍合金粉末和再生萤石矿。结果表明，该工艺实现了废水的达标排放，污泥产生量减少了14.79%，实现了铁铬镍的金属化还原，得到了再生萤石矿和金属品位93.62%的合金粉末，合金粉末中铁、铬、镍品位分别达69.31%, 7.60%和16.71%，回收率分别高达95.30%, 88.70%和97.53%。
An oxide layer is formed during stainlesssteel production and processing, which reduces the corrosion resistance of steel. At present, the common treatment for stainless steel strip surfaces is mainly pickling, using nitric and hydrofluoric acids to remove the oxide layer. After pickling, water is used to wash away the acids remaining on the surface of the stainless steel. A large number of stainless steel pickling wastewater will be produced, it contains heavy metal ions and fluoride ions and have great threat to the environment. The pickling wastewater is generally treated by lime neutralization, but the quantity of sludge is large and has difficulty in resource utilization. In this work, the law of fluorine ion removal and metal ion precipitation in stainless steel pickling wastewater system was studied, and a new process of calcium and sodium co-precipitation was developed to make the quality of wastewater achieve the standard, CaO and NaOH were added sequentially to achieve synergistic co-precipitation of harmful ions in wastewater, the sludge production was reduced by 14.79% as well. With the optimization of sedimentation method, the composition of sludge was also changed, which was beneficial to the subsequent reduction. The sludge reducted in 1200℃, realized the metallization of iron chromium nickel, metals and nonmetals were enriched in different areas, fine grinding and magnetic separation to get the regeneration of fluorite ore and alloy powder, the grade of metal was 93.62% . Grade of iron, chromium and nickel in alloy powder reached 69.31%, 7.60% and 16.71%, respectively, and their recovery rates were as high as 95.30%, 88.70% and 97.53%, respectively. The flow was short, energy consumption was low, and there did not produce secondary pollution in the new process, which had great significance to the innoxious disposal and recycle of stainless steel pickling wastewater.
[1] LI Xiao-ming，XIE Geng ,HOJAMBERDIEV Mirabbos.et al. Characterization and recycling of nickel-and chromium-contained picking sludge generated in production of stainless steel [J]. J.Cent.South Univ. 2014, 21:3241-3246
[2]高 亮。不锈钢酸洗废水处理中的污泥减排技术[J]中国给水排水，2009，25（10），83-86.
[3]杨才杰，刘福强，侯鹏等。不锈钢酸洗废水资源化处理技术进展与展望[J]工业水处理，2011，31（11），1-5.
[4] Xiaoming Li, Shangjie Wang, Junxue Zhao.et al. A Review on the Treatments and Minimization techniques of Stainless Steel Pickling Sludge. [J] Advanced Materials Research.2011. Vols.194-196: 2072-2076.
[5]殷志伟。含重金属离子酸性废水石灰石法处理后会用技术研究[J]，矿冶，2002，11（2），77-80.
[6]贺 慧,赵俊学,马红周,李小明.不锈钢酸洗废水处理技术分析[J]甘肃冶金，2009，31（5），42-46.
[7]阎 震.石灰石中和法在不锈钢酸洗废液中的优化设计[J]给水排水，2013，39（4），70-72.
[8]陈志国，简小龙，吴栋.不锈钢冷轧含酸、含铬废水处理重金属污泥回收技术研究,[J]工业水处理,2013,33(6):93-95.
[9]A.K.Minocha, N.Jain, C.L.Verma. Effect of organic materials on the solidification of heavy metal sludge [J].Construction and Building Materials, 2003,(17):17-81.
[10] Viguri J.;Andres A.;Ruiz C..Cement-waste and clay-waste derived products from metal hydroxides wastes: environmental characterization[J]. Process Safety and Environmental Protection, 2001,79(1):38-44.
[11]贾金平,杨骥.电镀重金属污泥的水泥固化稳定化处理[J].上海环境科学,1999,18(5):229-232.
[12] Roy A.Effect of Sodium Sulfite on Solidification Electroplating/Stabilization of a Synthetic Electroplating Sludge in Cementitious Binders[J]Journal of Hazardous Materials, 1992,30(3):297-316
[13]廖昌华,孙水裕,张志.焚烧温度对电镀污泥后续处理影响研究[J].再生资源,2002:(5):34-36.
[14]A.Roy, F.K.Cartledge. Long-term behavior of Portland cement-electroplating sludge waste from in presence of copper nitrate [J]. Journal of Hazardous Materials, 1997, (52): 265-286.
[15] Q. Gan. A case study of microwave processing of metal hydroxide sediment sludge from printed circuit board manufacturing wash water [J]. Waste Management, 2000, 20(8): 695-701.
[16]张英勇，概论重金属离子废水处理的机理与操作条件[J]有色金属加工，1997，3，50-53.
[17]陆智谋，重金属离子废水的石灰中和沉淀处理[J]工业用水与废水，1990，1，15-24.
[18]David?R.Lide, Handbook?of?Chemistry?and?Physics [M], 78th edition, 1997 –1998.