将混凝污泥碳化后制成电极材料，通过红外光谱和X射线衍射对污泥的官能团结构与晶型进行表征，采用循环伏安和线性扫描伏安法研究不同碳化温度下所制电极材料的电化学性能，并应用于电芬顿体系催化降解双酚A。结果表明，混凝污泥的主要成分为含碳和铁元素的复合物，高温碳化后污泥的结晶度增强。所制电极在电芬顿体系中显示出良好的电催化活性。外部投加Fe2+条件下，经900℃碳化的电极材料为阴极对双酚A的去除率最高，电解130 min后去除率高达99.2%。表明在电化学芬顿法废水处理中有一定的应用前景。
The resource utilization of coagulated sludge has a strong application potential. In this work, the actual coagulated sludge was recycled and carbonized at different temperatures to prepare electrode materials. The functional group structure and crystal form of sludge materials were characterized by Fourier transform infrared spectroscopy (FT-IR) and X-ray diffraction (XRD). The electrochemical properties of sludge electrode materials carbonized at different temperatures were studied by cyclic voltammetry (CV) and linear sweep voltammetry (LSV), and their electrocatalytic activities were evaluated and compared. Coagulated sludge treated by carbonization at high temperature was efficiently recovered and reused as high-performance cathode in electrochemical field, which was applied to the catalytic degradation of bisphenol A (BPA) in the Electro-Fenton system. The results showed that the main composition of coagulated sludge was carbon-iron complex, the crystallinity of sludge increased after carbonization at high temperature. According to evaluation by electrochemical characterization, the sludge treated by carbonization had a good hydrogen peroxide (H2O2) selectivity and yield. The selectivity of sludge electrodes carbonized at different temperatures for hydrogen peroxide in oxygen reduction reaction (ORR) process was more than 38%, the carbonized sludge presented a more rigorous two-electron transfer pathway and increased H2O2 selectivity. The removal rate of BPA increased by carbonized sludge material. Especially, coagulated sludge carbonized at 900℃ achieved 99.2% BPA removal in 130 min under the condition of adding Fe2+, due to its highly active two-electron reduction of oxygen (O2). The kinetics of BPA degradation by sludge material electrode was fitted, it was found that the kinetics of pollutant removal accorded with the first-order kinetics. The electrochemical characteristics of carbonized sludge electrode materials showed the possibility of their application in wastewater treatment by Electro-Fenton process. Also, a new way of synergistic treatment of sludge and wastewater pollutants has been developed, which has certain guiding significance in environmental treatment and sludge recovery.
[1]Oreshkin D V, Chebotaev A N, Perfilov V A.Disposal of Drilling Sludge in the Production of Building Materials [J].Procedia Engineering, 2015, 111(2015):607-611
[2]Johnson O A, Madzlan N, Kamaruddin I.Encapsulation of petroleum sludge in building blocks [J].Construction Building Materials, 2015, 78(2015):281-288
[3]Xu G, Yang X, Spinosa L.Development of sludge-based adsorbents: Preparation, characterization, utilization and its feasibility assessment [J]., 2015, 151(2015):221-232
[4]夏昊云, 刘培, 汤小芳.城市污泥制备水中重金属吸附剂及其吸附特性研究[J].再生资源与循环经济, 2014, 7(5):39-41
[5]Xia H Y, Liu P, Tang X F.Research on adsorption of heavy metal ions by activated carbon produced with sewage sludge [J]. Recycling Research. 2014, 7(5): 39-41.
[6]Chen T, Zhou Z, Xu S, et al.Adsorption behavior comparison of trivalent and hexavalent chromium on biochar derived from municipal sludge [J]. Bioresource technology, 2015, 190: 388-394.
[7]Kacan E.Optimum BET surface areas for activated carbon produced from textile sewage sludges and its application as dye removal [J]. Journal of environmental management, 2016, 166: 116-123.
[8]Devi P, Saroha A K.Simultaneous adsorption and dechlorination of pentachlorophenol from effluent by Ni–ZVI magnetic biochar composites synthesized from paper mill sludge [J]. Chemical Engineering Journal, 2015, 271: 195-203.
[9]曾祥专, 卢欢亮, 黄志华, 等.污泥生物炭用作除臭填料的试验研究[J].中国给水排水, 2013, 29(17):40-43
[10]Zeng X Z, Lu H L, Huang Z H, et al.Odor Removal by Using Sewage Sludge Biocarbon as Filter Material[J].China Water & Wastewater, 2013, 29(17):40-43
[11]徐仲榆, 范长岭, 苏玉长.石墨制品废料用作锂离子电池负极活性材料的研究 [J]. 炭素, 2004, 4: 3-9.
[12]Xu Z Y, Fan C L, Su Y C.Research on Using the processing graphite wastes as the negative electro active materials for Lithium batteries. [J]. Carbon, 2004, 4: 3-9.
[13]翟向乐.提钒废渣的浸出分离及制备锂离子电池电极材料的研究 [D]. 沈阳: 东北大学, 2014: 13-15..
[14]Zhai X L.The Research of Leaching Separation on Extracted Vanadium Residue and Preparation of Lithium-ion Battery Electrode Materials. [D]. Shen Yang: Northeastern University, 2014: 13-15.
[15] Cao Z Q, Zheng X, Cao H B, et al.Efficient reuse of anode scrap from lithium-ion batteries as cathode for pollutant degradation in electro-Fenton process: Role of different recovery processes[J].Chemical Engineering Journal, 2018, 337:256-264
[16]Casajus C, Abrego J, Marias F, et al.Product distribution and kinetic scheme for the fixed bed thermal decomposition of sewage sludge[J].Chemical Engineering Journal, 2009, 145(3):412-419
[17]Sellers R M.Spectrophotometric determination of hydrogen peroxide using potassium titanium (IV) oxalate[J].Analyst, 1980, 105(1255):950-954
[18]Fletcher A J, Uygur Y, Thomas K M.Role of surface functional groups in the adsorption kinetics of water vapor on microporous activated carbons[J].Journal of Physical Chemistry C, 2007, 111(23):8349-8359
[19]梁霍秀, 边玉珍, 叶世海, 等.氧化铁的制备及其电化学性能研究[J].南开大学学报, 2006, 39(3):43-46
[20]Liang H X, Bian Y Z, Ye S H, et al.The Preparation and Electrochemical Performance of Hemaite[J].Acta Scientiarum Naturalium Universitatis Nankaiensis(Natural Science Edition), 2006, 39(3):43-46
[21]姜文明.基于固废高分子材料制备多孔炭材料及其电化学性能研究 [D]. 镇江: 江苏大学, 2015: 4-7.
[22]Jiang W M.Study on the synthesis of porous carbon materials derived from polymer wastes and the electrochemical performance. [D]. Zhen Jiang: Jiangsu University, 2015: 4-7.
[23]Lan H, He W, Wang A, et al.An activated carbon fiber cathode for the degradation of glyphosate in aqueous solutions by the Electro-Fenton mode: Optimal operational conditions and the deposition of iron on cathode on electrode reusability [J]. Water Research, 2016, 105: 575-582.
[24]Wang Y, Zhao G, Chai S, et al.Three-Dimensional Homogeneous Ferrite-Carbon Aerogel: One Pot Fabrication and Enhanced Electro-Fenton Reactivity[J].Applied Materials, 2013, 5(3):842-852
[25]Jindarom C, Meeyoo V, Kitiyanan B, et al.Surface characterization and dye adsorptive capacities of char obtained from pyrolysisgasification of sewage sludge[J].Chemical Engineering Journal, 2007, 133(1-3):239-246